CARBON FILLED CONDUCTIVE EPOXY G6E-P
G6-Epoxy G6E-P is a two component electrically conductive epoxy for high performance bonding, sealing and coating. It can cure at room temperature or more rapidly at elevated temperatures. The optimum cure schedule is overnight at 25Â°C followed by 4 hours at 80Â°C. G6E-P has a thick paste consistency after mixing and bonds well to a wide variety of substrates including metals, composites, ceramics, and glass.
. TWO COMPONENT SYSTEM: Part A -Black paste, Part B - Black paste
. THE MIX RATIO: 100 (Part A) to 50 (Part B) by weight.
. CURING INSTRUCTIONS: Best results are obtained when product is cured at one of the following schedules: 24 hours @ 25Â°C, 5 hours @ 80Â°C or 2 hours @ 120Â°C
. COLOR: Black
. POT LIFE: 2 hours
. GLASS TRANSITION TEMPERATURE: 70Â°C
. MIXED VISCOSITY: 145-155 PaÂ·sec at 25Â°C/77Â°F
. HARDNESS, SHORE: >75 D
. VOLUME RESISTIVITY: ~ 5 Ohm x cm
. DENSITY: 1.0 -1.1 g/cm3