Product Description

SILVER/CARBON CONDUCTIVE EPOXY G6E-NS10

Conductive epoxies can be used to form an electrically conductive bond between dissimilar materials eliminating the need for soldering. Traditional silver-based epoxy materials require up to 80% weight load of silver fillers and as a result tend to be costly, brittle and prone to mechanical failure. 

Silver/Carbon Epoxy G6E-NS10  is a two component adhesive for high performance bonding, sealing and coating purposes. G6E-NS10 is intended to be cured at elevated temperatures. It can cure at room temperature in 60 hours or much more rapidly at elevated temperatures. Recommended curing temperature is 150°C. Volume resistivity of as low as 0.005  ohm cm can be achieved under optimum curing conditions.

PRODUCT INFORMATION

TWO COMPONENT SYSTEM: Part A - smooth thixotropic dark grey paste, Part B -smooth thixotropic silver paste.

THE MIX RATIO: 100 (Part A) to 100 (Part B) by weight.

CURING INSTRUCTIONS: Best results are obtained when product is cured at one of the following parameters: 60 hours @ 25°C, 3 hours @ 70°C or 1 hour @ 150°C

COLOR: Silver grey

POT LIFE: 4  hours

GLASS TRANSITION TEMPERATURE: 103°C (cured at 150°C)

MIXED VISCOSITY: 150 - 155 Pa·s at 25°C/77 F

HARDNESS, SHORE: >60D

VOLUME RESISTIVITY: Less than 0.005 ohm·cm 

For any further query please contact us.